The Al2O3 content of clay heat Clay insulating refractory bricks is generally more than 40%, and the Fe2O3 content is less than 2.0-2.5%. The clinker in the ingredients is 65-85%, and the combined clay is 35-15%. The crushed bonded clay and the finely ground clinker are mixed and milled, and then mixed with the granular clinker to make semi-dry mud, high pressure molding, and sintering at about 1400 ℃, with good performance.
Fireclay bricks are classified as weak acid refractories. Due to the large fluctuation range of chemical composition, different production methods, and differences in firing temperature, the properties of clay bricks change greatly.We can produce all kinds of Fireclay bricks according to customers' requirements
Fireclay bricksis suitable for supporting hot blast stoves of large, medium and small blast furnaces
low porosity clay bricks are mainly used in the regenerators of glass kilns. They can also be used in blast furnaces and hot blast furnaces in the steel industry; cement kilns in the building materials industry; chemical kilns in the chemical industry as kiln linings
The refractoriness of clay bricks is comparable to that of silica bricks, up to 1690~1730℃, but the softening temperature under load is more than 200℃ lower than that of silica bricks. Because in addition to the high refractory mullite crystal, the clay brick also contains nearly half of the low melting point amorphous glass phase.
The refractoriness of clay bricks is comparable to that of silica bricks, up to 1690~1730℃, but the softening temperature under load is more than 200℃ lower than that of silica bricks. Because in addition to the high refractory mullite crystal, the clay brick also contains nearly half of the low melting point amorphous glass phase.
Anhydrous taphole mud/taphole clay refers to taphole mud made of tar, resin, etc. as binders and corundum, bauxite, clay, silicon carbide, coke powder, etc. as raw materials. Anhydrous carbon taphole mud is made by a mud mill. When rolling, oil is added first, then block materials (clay and asphalt), and then powder materials (coke powder and clinker powder) are added after crushing. After pressing and mixing, the mud can be produced when it meets the standards.
Magnesia alumina bricks use periclase as the main crystal phase and magnesia-alumina spinel as the matrix. They are better in thermal shock resistance than magnesia bricks. In order to improve the thermal shock resistance of magnesia bricks, alumina or alumina is introduced into the ingredients. Bauxite clinker fine powder to form a magnesia-alumina sharp stone matrix, thereby making magnesia-alumina bricks
Corundum self flowing castable is a high-tech product developed according to the theory of solid fluid and combined with the application characteristics of refractory materials, which is the first in China. The corundum self-flowing material can be degassed and leveled without vibration with the help of its own gravity, so as to achieve densification.