High alumina castable is a refractory castable made of high alumina bauxite clinker as aggregate and refractory clay as powder, adding aluminate cement and sodium tripolyphosphate according to the formula proportion
Corundum bricks are mainly used in iron-making blast furnaces and blast furnace hot blast furnaces, refining furnaces outside steel-making furnaces, sliding water heaters, glass melting furnaces and petrochemical industrial furnaces, etc.
High alumina refractory mortars used in kilns in metallurgy, building materials, machinery, chemical industry, electric power and other industries, used for masonry clay bricks, high alumina bricks, corundum bricks, with full ash joints, good air tightness of masonry, high bonding strength, high temperature performance Excellent, suitable for construction time and so on.
low porosity clay bricks are mainly used in the regenerators of glass kilns. They can also be used in blast furnaces and hot blast furnaces in the steel industry; cement kilns in the building materials industry; chemical kilns in the chemical industry as kiln linings
The refractory ramming material is prepared from a high proportion of granular and powdery materials and a very low proportion of binders and other components, even all of which are composed of granules and powders, and are subject to strong ramming. Bulk materials for construction.
Insulating high alumina refractory bricks mainly refer to refractory products with an aluminum content of more than 48%. They are also called lightweight high-alumina bricks or heat-insulating high-alumina bricks due to their advantages of low bulk density, light weight, and good heat insulation effect. . It is a kind of thermal insulation refractory brick commonly used in high temperature industrial kilns and thermal equipment.
The Al2O3 content of clay heat Clay insulating refractory bricks is generally more than 40%, and the Fe2O3 content is less than 2.0-2.5%. The clinker in the ingredients is 65-85%, and the combined clay is 35-15%. The crushed bonded clay and the finely ground clinker are mixed and milled, and then mixed with the granular clinker to make semi-dry mud, high pressure molding, and sintering at about 1400 ℃, with good performance.
White corundum is made from industrial alumina powder, which is smelted in an arc at a high temperature above 2000 ℃ and then cooled. After crushing and shaping, magnetic separation to remove iron, it is divided into various particle sizes.
Brown corundum is made of natural bauxite as raw material, carbon (mainly coke) is used as reducing agent, and iron filings are added as sedimentation agent (clarifier) to form ferrosilicon deposited on the bottom of electric furnace.