The heavy part of the raw materials for the chrome zirconium corundum composite brick is sintered tabular corundum, high-purity chromium oxide, high-purity zircon, and Guangxi white cement.As the main raw material, the light part of the raw material is made of 47 mullite, kyanite, floating beads and coke gemstones as the main raw materials. During molding, a separator is set in the middle of the mold, and heavy materials and light materials are added at both ends. After high pressure molding , finished products made of high temperature sintering.
Chrome zirconium corundum composite brick for cement kilns
The heavy part of the raw materials for the chrome zirconium corundum composite brick is sintered tabular corundum, high-purity chromium oxide, high-purity zircon, and Guangxi white cement.
As the main raw material, the light part of the raw material uses 47 mullite, kyanite, drift beads and coke gemstones as the main raw materials.
A spacer plate is arranged between, and heavy materials and light materials are added at both ends, and the finished product is made by high pressure molding and high temperature sintering.
product name |
Chrome zirconium corundum composite brick |
|
chemical composition |
Al2O3 |
≥80 |
Fe2O3 |
≤0.6 |
|
Cr2O3+ZrO2 |
≥8 |
|
Bulk density (g/cm3) |
≥3.1 |
|
Apparent porosity(%) |
≤16 |
|
Compressive strength(MPa) |
≥130 |
|
0.2MPasoftening temperature under load(℃) |
≥1700 |
|
Thermal shock stability,1100℃ |
≥25 |
Chrome zirconium corundum composite brick has:
Wear-resistant and erosion-resistant
Stable high temperature performance,
Thermal shock stability and other characteristics.
At the same time, it also has the properties of resistance to the erosion of sulfur, chlorine and alkaline salts, and is widely used in high temperature thermal equipment such as the lining of rotary kilns in waste incineration production lines.
Corundum bricks are mainly used in iron-making blast furnaces and blast furnace hot blast furnaces, refining furnaces outside steel-making furnaces, sliding water heaters, glass melting furnaces and petrochemical industrial furnaces, etc.
The heavy parts of the chrome-zirconium mullite composite bricks are made of high-purity sintered mullite, high-purity chromium oxide, high-purity zirconia, and Guangbai mud as the main raw materials, and the light part of the raw materials are made of 47 mullite, kyanite, Bleaching beads, coke gemstones and Guangxi white mud are the main raw materials
Chrome corundum brick refers to corundum refractory products containing Cr2O3. At high temperature, Cr2O3 and Al2O3 form a continuous solid solution, so the high temperature performance of chromium corundum products is better than that of pure corundum products. Chromium corundum products are widely used, and the content of Cr2O3 is mostly in the range of 9% to 15%.
Brown corundum refractory brick is made of fused corundum as the main raw material. It is formed by high pressure and fired at high temperature. It has high thermal shock stability, low porosity, low expansion, good resistance to melt vapor and gas erosion, and excellent oxidation resistance. Dimensionally accurate advantages.
The refractory ramming material is prepared from a high proportion of granular and powdery materials and a very low proportion of binders and other components, even all of which are composed of granules and powders, and are subject to strong ramming. Bulk materials for construction.
Acid resistant refractory gunning material is used for spraying of blast furnaces, hot blast stoves, hot blast pipes, flue protection layers, working layers, etc.
The Al2O3 content of clay heat Clay insulating refractory bricks is generally more than 40%, and the Fe2O3 content is less than 2.0-2.5%. The clinker in the ingredients is 65-85%, and the combined clay is 35-15%. The crushed bonded clay and the finely ground clinker are mixed and milled, and then mixed with the granular clinker to make semi-dry mud, high pressure molding, and sintering at about 1400 ℃, with good performance.
Converter, electric furnace gunning material has the characteristics of high adhesion rate, good high temperature corrosion resistance, etc.
Corundum bricks are mainly used in iron-making blast furnaces and blast furnace hot blast furnaces, refining furnaces outside steel-making furnaces, sliding water heaters, glass melting furnaces and petrochemical industrial furnaces, etc.
The heavy parts of the chrome-zirconium mullite composite bricks are made of high-purity sintered mullite, high-purity chromium oxide, high-purity zirconia, and Guangbai mud as the main raw materials, and the light part of the raw materials are made of 47 mullite, kyanite, Bleaching beads, coke gemstones and Guangxi white mud are the main raw materials
Chrome corundum brick refers to corundum refractory products containing Cr2O3. At high temperature, Cr2O3 and Al2O3 form a continuous solid solution, so the high temperature performance of chromium corundum products is better than that of pure corundum products. Chromium corundum products are widely used, and the content of Cr2O3 is mostly in the range of 9% to 15%.
Brown corundum refractory brick is made of fused corundum as the main raw material. It is formed by high pressure and fired at high temperature. It has high thermal shock stability, low porosity, low expansion, good resistance to melt vapor and gas erosion, and excellent oxidation resistance. Dimensionally accurate advantages.
The refractory ramming material is prepared from a high proportion of granular and powdery materials and a very low proportion of binders and other components, even all of which are composed of granules and powders, and are subject to strong ramming. Bulk materials for construction.
Acid resistant refractory gunning material is used for spraying of blast furnaces, hot blast stoves, hot blast pipes, flue protection layers, working layers, etc.
The Al2O3 content of clay heat Clay insulating refractory bricks is generally more than 40%, and the Fe2O3 content is less than 2.0-2.5%. The clinker in the ingredients is 65-85%, and the combined clay is 35-15%. The crushed bonded clay and the finely ground clinker are mixed and milled, and then mixed with the granular clinker to make semi-dry mud, high pressure molding, and sintering at about 1400 ℃, with good performance.
Converter, electric furnace gunning material has the characteristics of high adhesion rate, good high temperature corrosion resistance, etc.
Corundum bricks are mainly used in iron-making blast furnaces and blast furnace hot blast furnaces, refining furnaces outside steel-making furnaces, sliding water heaters, glass melting furnaces and petrochemical industrial furnaces, etc.
The heavy parts of the chrome-zirconium mullite composite bricks are made of high-purity sintered mullite, high-purity chromium oxide, high-purity zirconia, and Guangbai mud as the main raw materials, and the light part of the raw materials are made of 47 mullite, kyanite, Bleaching beads, coke gemstones and Guangxi white mud are the main raw materials
Chrome corundum brick refers to corundum refractory products containing Cr2O3. At high temperature, Cr2O3 and Al2O3 form a continuous solid solution, so the high temperature performance of chromium corundum products is better than that of pure corundum products. Chromium corundum products are widely used, and the content of Cr2O3 is mostly in the range of 9% to 15%.
Brown corundum refractory brick is made of fused corundum as the main raw material. It is formed by high pressure and fired at high temperature. It has high thermal shock stability, low porosity, low expansion, good resistance to melt vapor and gas erosion, and excellent oxidation resistance. Dimensionally accurate advantages.
The refractory ramming material is prepared from a high proportion of granular and powdery materials and a very low proportion of binders and other components, even all of which are composed of granules and powders, and are subject to strong ramming. Bulk materials for construction.
Acid resistant refractory gunning material is used for spraying of blast furnaces, hot blast stoves, hot blast pipes, flue protection layers, working layers, etc.
The Al2O3 content of clay heat Clay insulating refractory bricks is generally more than 40%, and the Fe2O3 content is less than 2.0-2.5%. The clinker in the ingredients is 65-85%, and the combined clay is 35-15%. The crushed bonded clay and the finely ground clinker are mixed and milled, and then mixed with the granular clinker to make semi-dry mud, high pressure molding, and sintering at about 1400 ℃, with good performance.
Converter, electric furnace gunning material has the characteristics of high adhesion rate, good high temperature corrosion resistance, etc.