Anti stripping high alumina bricks are referred to as anti-stripping bricks or anti-stripping refractory bricks. Anti-stripping high-alumina bricks are widely used in my country's new dry process kiln, Libore kiln and wet process kiln, including kiln door cover, rising flue, cooling zone, decomposition zone, safety belt, transition zone, coolant rear Walls and side walls and beams with curved ceilings.

The Al2O3 content of clay heat Clay insulating refractory bricks is generally more than 40%, and the Fe2O3 content is less than 2.0-2.5%. The clinker in the ingredients is 65-85%, and the combined clay is 35-15%. The crushed bonded clay and the finely ground clinker are mixed and milled, and then mixed with the granular clinker to make semi-dry mud, high pressure molding, and sintering at about 1400 ℃, with good performance.

Anhydrous taphole mud/taphole clay refers to taphole mud made of tar, resin, etc. as binders and corundum, bauxite, clay, silicon carbide, coke powder, etc. as raw materials. Anhydrous carbon taphole mud is made by a mud mill. When rolling, oil is added first, then block materials (clay and asphalt), and then powder materials (coke powder and clinker powder) are added after crushing. After pressing and mixing, the mud can be produced when it meets the standards.

The chemical composition of bauxite is mainly Al2O3, SiO2, Fe2O3, TO2, accounting for about 95% of the total composition, and the secondary components are CaO, MgO, K2O, Na20, S, MnO2 organic matter and trace components Ga, Ge, etc.

silicon mullite brick is a kind of refractory brick product made of super high alumina bauxite and silicon carbide as raw materials through a special sintering process. It has the characteristics of continuously forming a protective layer and reducing ring formation, and its heat resistance is also very good. The softening temperature under load can reach 1600 ℃, and the service life is long. Mainly used in the transition zone, decomposition zone and cooler of small and medium-sized cement kilns.

Anti stripping high alumina bricks are referred to as anti-stripping bricks or anti-stripping refractory bricks. Anti-stripping high-alumina bricks are widely used in my country's new dry process kiln, Libore kiln and wet process kiln, including kiln door cover, rising flue, cooling zone, decomposition zone, safety belt, transition zone, coolant rear Walls and side walls and beams with curved ceilings.

The Al2O3 content of clay heat Clay insulating refractory bricks is generally more than 40%, and the Fe2O3 content is less than 2.0-2.5%. The clinker in the ingredients is 65-85%, and the combined clay is 35-15%. The crushed bonded clay and the finely ground clinker are mixed and milled, and then mixed with the granular clinker to make semi-dry mud, high pressure molding, and sintering at about 1400 ℃, with good performance.

Anhydrous taphole mud/taphole clay refers to taphole mud made of tar, resin, etc. as binders and corundum, bauxite, clay, silicon carbide, coke powder, etc. as raw materials. Anhydrous carbon taphole mud is made by a mud mill. When rolling, oil is added first, then block materials (clay and asphalt), and then powder materials (coke powder and clinker powder) are added after crushing. After pressing and mixing, the mud can be produced when it meets the standards.

The chemical composition of bauxite is mainly Al2O3, SiO2, Fe2O3, TO2, accounting for about 95% of the total composition, and the secondary components are CaO, MgO, K2O, Na20, S, MnO2 organic matter and trace components Ga, Ge, etc.

silicon mullite brick is a kind of refractory brick product made of super high alumina bauxite and silicon carbide as raw materials through a special sintering process. It has the characteristics of continuously forming a protective layer and reducing ring formation, and its heat resistance is also very good. The softening temperature under load can reach 1600 ℃, and the service life is long. Mainly used in the transition zone, decomposition zone and cooler of small and medium-sized cement kilns.

Silicon carbide used in industry is a synthetic material, commonly known as emery. Silicon carbide is one of the most commonly used non-oxide refractory raw materials in the field of refractories.